Pengerasan Permukaan Baja Perkakas HSS M41 dengan Teknik Pelapisan Metal Spray
DOI:
https://doi.org/10.26874/jt.vol1no2.205Keywords:
Metal Spray, Heat Treatment, Diffusion and Wear ResistanceAbstract
Intermetallic compound Fe-AL has good strength and hardness properties. Those properties were required Io improve the wear resistance of component which its application always contact with another part like cutting tool in machining processes. This experiment was carried out to improve the wear resistance of metal, which in this case is high-speed steel (HSS M41). This preliminary experiment was focused on to form the Intermetallic compound Fe-Al layer in the surface Of the steel, This layer was obtained by metal spray technique in which Al-Si spray to the surface of base metal HSS M41 and then heat-treated at 850oC, The holding time of heat treatment for 4 hours, 6 hours and 8 hours respectively was used, Experimental results showed holding time of heat treatment process was influenced to forming the intermetallic layer, thickness and hardness was specimen with heat-treated at 850 OC and holding time 8 hours exhibit the maximum hardness of 1120 HV and also increase the lifetime from 1.84 days to 14.125 days. The thickness of intermetallic layer was 0.81 mm.
References
2. Begemen ML, "Manufacturing Processes", Jhon Wiley, London 1957 3. Calister, Jr, " Material's Science and Engineering an Introduction" Jhon Wiley & Son Inc, 1985
4. Smallman RE, " Modem Physical Metallurgy", Betterworths, London, 1976.
5. ASM Metal Handbook, "Surface Cleaning, Finishing and Coating", Vol.5, Ninth Edition 1982
6. ASM Metal Handbook, " Properties and Selection Stainless Steel, Tool Material and Special Purpose Metal ", Vol.3, Ninth Edition 1982.
7. Robert GA, Harnaker JR, Jhonson AR, 11 Tool Steel", ASM Handbook, Third Edition 1962
8. Saubari A K" Pelapisan Al Pada &kja Dengan Proses Metal Spray", Departemen Teknik Mesin ITB 1991
9. Schaffer J.P," The Science and Design of Engineering Material", WCB/Mc Graw -Hill, 1999
Additional Files
Published
Issue
Section
License
Penulis yang menyerahkan artikel di Jurnal Teknik: Media Pengembangan dan Aplikasi Teknik untuk keperluan publikasi telah mengetahui bahwa Jurnal Teknik: Media Pengembangan dan Aplikasi Teknik memberikan akses terbuka terhadap konten untuk mendukung pertukaran informasi mengenai ilmu pengetahuan, sesuai dengan penerbitan daring yang berbasis Open Access Journal dan mengikuti Creative Commons Attribution 4.0 International License. Sehingga penulis setuju dengan ketentuan-ketentuan berikut:
1. Penulis memegang hak cipta dan memberikan hak publikasi pertama kepada pihak jurnal dengan pekerjaan secara bersamaan
di bawah Creative Commons Attribution 4.0 International License yang memungkinkan orang lain untuk berbagi pekerjaan
dengan pengakuan kepengarangan karya dan publikasi pertama artikel tersebut di Jurnal Teknik: Media Pengembangan dan
Aplikasi Teknik.
2. Penulis dapat melakukan perjanjian tambahan untuk hak distribusi non-eksklusif artikel yang telah diterbitkan di jurnal ini
(misalnya, posting ke sebuah repositori institusi atau menerbitkannya dalam sebuah buku), dengan mengakui bahwa
publikasi pertama dilakukan di Jurnal Teknik: Media Pengembangan dan Aplikasi Teknik.
3. Penulis diizinkan dan didorong untuk menyebarkan karya mereka secara daring (misalnya, dalam repositori institusi atau
laman web penulis) setelah artikel terbit (proses penerbitan artikel selesai). Hal ini terkait dengan imbas dari pertukaran
informasi yang produktif (Lihat Pengaruh Open Access).