Dehidrasi Etanol Menggunakan Zeolit Teraktivasi Irradiasi Lampu Sinar Ultraviolet (UV Light) pada Kolom Fixed Bed

Authors

  • M. Praditia Ansor University of Lampung
  • Simparmin Br. Ginting Universitas Lampung
  • Muhammad Haviz Universitas Lampung
  • Darmansyah Universitas Lampung

DOI:

https://doi.org/10.55893/jt.vol21no1.442

Keywords:

Lampung Natural Zeolit (ZAL), Activation, UV, Characteristic, Adsorption

Abstract

To obtain ethanol purity >99.5%, an adsorption method using Lampung Natural Zeolite (ZAL) is needed. In order to be used as a zeolite adsorbent, activation must be carried out using UV light lamp irradiation germicidal lamp 254 nm, blacklight lamp 360 nm and insect lamp 546 nm. The results of the BET characteristic test showed that the surface area of ??the non-treated zeolite was 41,331 m2/g, the germicidal lamp was 41,158 m2/g, the black light lamp was 40,399 m2/g and the insect lamp was 38,796 m2/g. The largest total pore volume was obtained from UV germicidal lamp activated zeolite 0.0690 cc/gram and the average pore size was found in insect lamp activated zeolite 35.57. After the activation of the zeolite, pellets were formed using a binder from wheat flour with a composition of 35% by weight of zeolite, then the zeolite was calcined to remove the binder that was still attached and opened the pores that were closed by the binder. The results obtained were dehydrated ethanol to increase purity using zeolite activated by UV germicidal lamp 98.69% v/v for 45 minutes, blacklight and insect lamp 98.69% v/v for 55 minutes.

Author Biographies

  • Simparmin Br. Ginting, Universitas Lampung

    Jurusan Teknik Kimia

  • Muhammad Haviz, Universitas Lampung

    Jurusan Teknik Kimia

  • Darmansyah, Universitas Lampung

    Jurusan Teknik Kimia

References

Amrbroz F., Macdonald T.J., Martis V., Parkin I. P., (2018). Evaluation of The BET Theory for the Characterization of Meso and Microporous Mos. Amerika Serikat. Wiley Online Library.

Deepak P., S., Dilli R., R., Raju B., T., (2009). Effect of UV-Treatment On The Wettability of Polycarbonate. Kathmandu University Journal of Science, Engineering and Technology Vol. 5, No. II, September, 2009, Hal. 37-41.

Florea, C., G. BrĂTucu. (2012). "Possibilities of using the germicidal effect of UV-C light for disinfecting the water used in food industry." Bulletin of the Transilvania University of Brasov 5 (54). Hal. 147-154.

Geankoplis, C, J,. 1993. Transport Processes and Unit Operations. 3rd edition. Prentice-Hall, Inc. A Simon & Schuster Company. United States of America. Hal. 701-702.

Handrian, Budi Wahyu S. and Mindaryani A., (2017). Adsorpsi Air dari Campuran Uap Etanol-Air dengan Zeolit Sintesis 4A Pada Packet Bed Dalam Rangka Produksi Fuel Grade Etanol. Jurnal Rekayasa Proses, Vol. 11, No. 2, Hal. 68-77. Yogyakarta.

Jankowska, H., Swiatkowski, A. dan Choma, J. (1991). Active Carbon. London : Horwood.

Kowalski, W. (2009), Ultraviolet Germicidal Irradiation handbook. Sringer-Verlag. Berlin Heidelberg

Marwan F., Suhartana, Pardoyo. (2015). Zeolit Alam Termodifikasi Logam Fe sebagai Adsorben Fosfat (PO43-) pada Air Limbah. Semarang. Jurnal Kimia Sains dan Aplikasi 18 (3) (20015) Hal. 94.

Ma’ruf, A., dan Mulyadi, A.H., 2010, “Pembuatan Zeolit Pelet Sebagai Adsorben Pada Pembuatan Bioetanol Tradisional”, Laporan Penelitian, Program Studi Teknik Kimia, UMP, Purwokerto.

Mazur M, Eliasova P C, Roth WJ, Cejka J. (2014), Intercalation chemistry of layered zeolite precursor IPC

Miller, S. L., J. Linnes . (2013). Ultraviolet Germicidal Irradiation: Future Direction for Air Desinfection and Building Application. Photochemistry and Photobiology 89(4). Hal. 777 – 781

Nurdyastuti, I. (2005). Teknologi Proses Produksi Bio-Ethanol. Prospek pengembangan bio-fuel sebagai substitusi bahan bakar minyak.

Perry, R.H., and Green, D.W., (1997). Perry’s Chemical Engineer’s Handbook, 7th Edition, Hal.1128, 1490-1497, 1534-1537, Mc Graw-Hill Co, New York.

Santi, K. (2010). Zeolit In Industrial Separation And Catalysis, Process Engineering Channel, Wiley-VCH Verlag GmbH &Co. KgaA, Weinheim USA.

Setyawan P. Sakti, Masruroh, Nike H., (2017). Effect UV Radiation duration and Moleculer Wieght to Hidropobicity and Surface Roughness of Polystyrene Coating On QCM sensor. Jurnal Teknologi. Hal. 61-67. Departement of Physics, Faculty of Mathematics and Natural Sciences, Brawijaya University, Jl. Veteran, Malang 65145, Indonesia.

Slamet, Ellyana M., dan Bismo S., (2018). Modifikasi Zeolit Alam Lampung dengan Fotokatalisis TiO2 Melalui Metode Sol Gel dan Aplikasinya Untuk Penyisihan Fenol. Depatemen Teknik Kimia, Fakultas Teknik, Universitas Indonesia. Hal. 2-3. Depok.

Thommes, M., Kaneko, K., Neimark, A.V., Olivier, J.P., Rodriguez-Reinoso, F., Rouquerol, J. and Sing, K.S. (2015) Physisorption of Gases, with Special Reference to the Evaluation of Surface Area and Pore Size Distribution (IUPAC Technical Report). Pure and Applied Chemistry, 87, 1051-1069.

Additional Files

Published

2022-07-05

How to Cite

Dehidrasi Etanol Menggunakan Zeolit Teraktivasi Irradiasi Lampu Sinar Ultraviolet (UV Light) pada Kolom Fixed Bed. (2022). Jurnal Teknik: Media Pengembangan Ilmu Dan Aplikasi Teknik, 21(1), 64-73. https://doi.org/10.55893/jt.vol21no1.442

Similar Articles

21-30 of 47

You may also start an advanced similarity search for this article.